Industrial Solution

MiiCraft industrial solution offers the stable printing materials coming with the constant parameters.

 

 

No.ModelResinPrinting parameter Post-procedurePrint-out examples
Functional Parts
1Adv. 205BV-023Thickness : 100um
Speed : slow
Curing time : 13.5s
Gap : 0mm
Base curing : 35s
Base Layer : 1
Buffer layer : 6
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 600s
2Adv. 205BV-023Thickness : 100um
Speed : slow
Curing time : 13.5s
Gap : 0mm
Base curing : 35s
Base Layer : 1
Buffer layer : 8
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 600s
3Adv. 205BV-023Thickness : 100um
Speed : slow
Curing time : 13.5s
Gap : 0mm
Base curing : 35s
Base Layer : 1
Buffer layer : 10
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 600s
4M150BV-023Thickness : 100um
Speed : slow
Curing time : 12.5s
Gap : 0mm
Base curing : 35s
Base Layer : 1
Buffer layer : 10
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 300s
5Adv. 255BV-022Thickness : 50um
Speed : normal
Curing time : 2s
Gap : 0
Base curing : 15s
Base Layer : 1
Buffer layer : 4
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 600s
6Adv. 255BV-022Thickness : 50um
Speed : normal
Curing time : 2s
Gap : 0
Base curing : 18s
Base Layer : 1
Buffer layer : 4
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 600s
7Adv. 255BV-022Thickness : 100um
Speed : normal
Curing time : 3.5s
Gap : 0
Base curing : 18s
Base Layer : 1
Buffer layer : 4
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 900s
8Adv. 255BV-022Thickness : 100um
Speed :normal
Curing time : 3.7s
Gap : 0
Base curing : 18s
Base Layer : 1
Buffer layer : 4
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 900s
9Adv. 255BV-022Thickness : 100um
Speed :normal
Curing time : 3.4s
Gap : 0
Base curing : 16s
Base Layer : 1
Buffer layer : 4
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 600s
10Adv. 205BV-022Thickness : 100um
Speed : slow
Curing time : 2.5s
Gap : 0
Base curing : 15s
Base Layer : 1
Buffer layer : 4
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 600s
11Adv. 205BV-022Thickness : 100um
Speed : slow
Curing time : 2.5s
Gap : 0
Base curing : 20s
Base Layer : 1
Buffer layer : 8
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 600s
12Adv. 205BV-022Thickness : 100um
Speed : slow
Curing time : 2.5s
Gap : 0
Base curing : 15s
Base Layer : 1
Buffer layer : 6
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 900s
13M125BV-022Thickness : 50um
Speed : slow
Curing time : 1.2s
Gap : 0
Base curing : 15s
Base Layer : 1
Buffer layer : 4
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 300s
14M150BV-022Thickness : 50um
Speed : slow
Curing time : 1.5s
Gap : 0
Base curing : 15s
Base Layer : 1
Buffer layer : 4
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 600s
Total layers : 820
Time : 4hr30
15M150BV-022Thickness : 50um
Speed : slow
Curing time : 1.4s
Gap : 0
Base curing : 12s
Base Layer : 1
Buffer layer : 4
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 480s
16M150BV-022Thickness : 50um
Speed : slow
Curing time : 1.4s
Gap : 0
Base curing : 15s
Base Layer : 1
Buffer layer : 4
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 300s
17Adv. 255BASF X004MThickness : 50um
Speed : slow
Curing time : 3.6s
Gap : 0
Base curing : 18s
Base Layer : 1
Buffer layer : 4
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 900s
18Adv. 255BASF X004MThickness : 50um
Speed : slow
Curing time : 3.6s
Gap : 0
Base curing : 18s
Base Layer : 1
Buffer layer : 4
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 1200s
19Adv. 205BASF X004MThickness : 50um
Speed : slow
Curing time : 3s
Gap : 0
Base curing : 15s
Base Layer : 1
Buffer layer : 10
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 600s
20Adv. 205BASF X004MThickness : 50um
Speed : slow
Curing time : 2.8s
Gap : 0
Base curing : 15s
Base Layer : 1
Buffer layer : 8
Wash : Alcohol
Post-Curing Energy : 30mw/cm2
Post-Curing time : 600s
Total layers :440
Time : 2hr20